Solid state lighting devices with cellular arrays and associated methods of manufacturing

ABSTRACT

Solid state lighting (“SSL”) devices with cellular arrays and associated methods of manufacturing are disclosed herein. In one embodiment, a light emitting diode includes a semiconductor material having a first surface and a second surface opposite the first surface. The semiconductor material has an aperture extending into the semiconductor material from the first surface. The light emitting diode also includes an active region in direct contact with the semiconductor material, and at least a portion of the active region is in the aperture of the semiconductor material.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. application Ser. No. 13/612,484 filed Sep. 12, 2012, now U.S. Pat. No. 8,709,845, which is a divisional of U.S. application Ser. No. 12/731,923 filed Mar. 25, 2010, now U.S. Pat. No. 8,390,010, each of which is incorporated herein by reference in its entirety.

TECHNICAL FIELD

The present technology is directed generally to solid state lighting (“SSL”) devices with cellular arrays and associated methods of manufacturing.

BACKGROUND

SSL devices generally use semiconductor light emitting diodes (“LEDs”), organic light-emitting diodes (“OLEDs”), and/or polymer light emitting diodes (“PLEDs”) as sources of illumination rather than electrical filaments, a plasma, or a gas. FIG. 1 is a cross-sectional diagram of a portion of a conventional indium-gallium nitride (“InGaN”) LED 10. As shown in FIG. 1, the LED 10 includes a substrate 12 (e.g., silicon carbide, sapphire, gallium nitride, or silicon), an N-type gallium nitride (“GaN”) material 14, an InGaN/GaN multiple quantum wells (“MQWs”) 16, and a P-type GaN material 18 layered on one another in series. The LED 10 also includes a first contact 20 on the P-type GaN material 18 and a second contact 22 on the N-type GaN material 14.

According to conventional techniques, the N-type and/or P-type GaN materials 14 and 18 are typically formed as planar structures via epitaxial growth. The planar structures have limited surface areas and thus can limit the number of MQWs formed thereon. As a result, the LED 10 may have limited emission power output per unit surface area. Accordingly, several improvements to increase the emission output for a particular surface area of an LED may be desirable.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of a portion of an LED in accordance with the prior art.

FIGS. 2A-2F are schematic perspective views of various crystal planes in a GaN/InGaN material in accordance with embodiments of the technology.

FIGS. 3A-3H are partially cutaway and perspective views of a portion of a semiconductor device undergoing a process to form an SSL device in accordance with embodiments of the technology.

DETAILED DESCRIPTION

Various embodiments of SSL devices and associated methods of manufacturing are described below. The term “microelectronic substrate” is used throughout to include substrates upon which and/or in which SSL devices, microelectronic devices, micromechanical devices, data storage elements, read/write components, and other features are fabricated. A person skilled in the relevant art will also understand that the technology may have additional embodiments, and that the technology may be practiced without several of the details of the embodiments described below with reference to FIGS. 2A-3H.

In the following discussion, an LED having GaN/InGaN materials is used as an example of an SSL device in accordance with embodiments of the technology. Several embodiments of the SSL device may also include at least one of gallium arsenide (GaAs), aluminum gallium arsenide (AlGaAs), gallium arsenide phosphide (GaAsP), aluminum gallium indium phosphide (AlGaInP), gallium(III) phosphide (GaP), zinc selenide (ZnSe), boron nitride (BN), aluminum nitride (AlN), aluminum gallium nitride (AlGaN), aluminum gallium indium nitride (AlGaInN), and/or other suitable semiconductor materials.

FIGS. 2A-2F are schematic perspective views of various crystal planes in a portion of a GaN/InGaN material. In FIGS. 2A-2F, Ga (or Ga/In) and N atoms are schematically shown as large and small spheres, respectively. As shown in FIGS. 2A-2F, the GaN/InGaN material has a wurtzite crystal structure with various lattice planes or facets as represented by corresponding Miller indices. A discussion of the Miller index can be found in the Handbook of Semiconductor Silicon Technology by William C. O'Mara. For example, as shown in FIG. 2A, the plane denoted as the “c-plane” in the wurtzite crystal structure with a Miller index of (0001) contains only Ga atoms. Similarly, other planes in the wurtzite crystal structure may contain only N atoms and/or other suitable types of atoms. In another example, the wurtzite crystal structure also includes crystal planes that are generally perpendicular to the c-plane. FIG. 2B shows a plane denoted as the “a-plane” in the wurtzite crystal structure with a Miller index of (11 20). FIG. 2C shows another plane denoted as the “m-plane” in the wurtzite crystal structure with a Miller index of (10 10). In a further example, the wurtzite crystal structure can also include crystal planes that are canted relative to the c-plane without being perpendicular thereto. As shown in FIGS. 2D-2F, each of the planes with Miller indices of (10 13), (10 11), and (11 22) form an angle with the c-plane shown in FIG. 2A. The angle is greater than 0° but less than 90°. Even though only particular examples of crystal planes are illustrated in FIGS. 2A-2F, the wurtzite crystal structure can also include other crystal planes not illustrated in FIGS. 2A-2F.

FIG. 3A is a partially cutaway and perspective view of a portion of a semiconductor device 100 undergoing a process in accordance with embodiments of the technology. As shown in FIG. 3A, an initial stage of the process includes forming one or more optional first and second buffering materials 104 a and 104 b and a first semiconductor material 106 on a microelectronic substrate 102 in series. The microelectronic substrate 102 can include a substrate material upon which the first and second buffering layers 104 a and 104 b and the first semiconductor material 106 can be readily formed. For example, in one embodiment, the microelectronic substrate 102 includes silicon (Si) with a lattice orientation of {1,1,1}. In other embodiments, the microelectronic substrate 102 can include gallium nitride (GaN), aluminum nitride (AlN), and/or other suitable semiconductor materials. In further embodiments, the microelectronic substrate 102 can include diamond, glass, quartz, silicon carbide (SiC), aluminum oxide (Al₂O₃), and/or other suitable crystalline and/or ceramic materials.

The optional first and second buffer materials 104 a and 104 b may facilitate formation of the first semiconductor material 106 on the microelectronic substrate 102. In certain embodiments, the first and second buffer materials 104 a and 104 b can include aluminum nitride (AlN) and aluminum gallium nitride (AlGaN), respectively. In other embodiments, the first and second buffer materials 104 a and 104 b can also include aluminum oxide (Al₂O₃), zinc nitride (Zn₃N₂), and/or other suitable buffer materials. In further embodiments, at least one of the first and second buffer materials 104 a and 104 b may be omitted.

In the illustrated embodiment, the first semiconductor material 106 can include an N-type GaN material formed on the optional second buffer material 104 b. The first semiconductor material 106 has a first surface 106 a in direct contact with the second buffer material 104 b and a second surface 106 b opposite the first surface 106 a. In other embodiments, the first semiconductor material 106 can also include a P-type GaN material and/or other suitable semiconductor materials. In any of the foregoing embodiments, the first and second buffer materials 104 a and 104 b and the first semiconductor material 106 may be formed on the microelectronic substrate 102 via metal organic CVD (“MOCVD”), molecular beam epitaxy (“MBE”), liquid phase epitaxy (“LPE”), hydride vapor phase epitaxy (“HVPE”), and/or other suitable techniques.

As shown in FIG. 3A, another stage of the process can include depositing and patterning a mask material 108 on the first semiconductor material 106 to form at least one aperture 110 in the mask material 108. In the illustrated embodiment, the apertures 110 each include generally cylindrical openings extending substantially through the entire depth of the mask material 108 and exposing a portion of the second surface 106 b of the first semiconductor material 106. In other embodiments, the apertures 110 may also include openings with hexagonal, pentagonal, oval, rectilinear, square, triangular, and/or other suitable cross sections that extend at least partially into the mask material 108. In further embodiments, the apertures 110 may have openings with a combination of different cross sections that extend to different depths in the mask material 108.

In certain embodiments, the mask material 108 can include a photoresist deposited on the first semiconductor material 106 via spin coating and/or other suitable techniques. The deposited photoresist may then be patterned via photolithography. In other embodiments, the mask material 108 may also include silicon oxide (SiO₂), silicon nitride (SiN), and/or other suitable masking materials formed on the first semiconductor material 106 via chemical vapor deposition (“CVD”), atomic layer deposition (“ALD”), and/or other suitable techniques. In such embodiments, the deposited masking materials may then be patterned with a photoresist (not shown) via photolithography and subsequently etched (e.g., dry etching, wet etching, etc.) to form the apertures 110.

FIGS. 3B and 3C show embodiments of another stage of the process in which at least one well 112 is formed in the first semiconductor material 106. The wells 112 can individually correspond to the apertures 110 (FIG. 3A) in the mask material 108 (FIG. 3A). As shown in FIG. 3B, the wells 112 individually include a generally hexagonal cross section with six sidewalls 114 extending from the second surface 106 b toward the first surface 106 a of the first semiconductor material 106. The sidewalls 114 of the individual wells 112 are joined at a generally planar base 116 at a depth within the semiconductor material 106 intermediate to the first and second surfaces 106 a and 106 b. In other embodiments, at least one of the wells 112 may include sidewalls 114 that extend the entire length between the first and second surfaces 106 a and 106 b of the first semiconductor material 106. In further embodiments, the base 116 may not be planar, as described in more detail below with reference to FIG. 3C.

The wells 112 may be formed via an isotropic, an anisotropic, or a combination of both isotropic and anisotropic etching operations. For example, in certain embodiments, forming the wells 112 includes isotropically etching and subsequently anisotropically etching the first semiconductor material 106 via the apertures 110 of the mask material 108 (FIG. 3A.) The isotropic etching may include contacting the first semiconductor material 106 with phosphoric acid (H₃PO₄), sodium hydroxide (NaOH), potassium hydroxide (KOH), and/or other suitable etchants. The anisotropic etching may include plasma etching, reactive ionic etching, and/or other suitable dry etching techniques. After forming the wells 112, the mask material 108 may be removed via wet etching, laser ablation, and/or other suitable techniques.

Without being bound by theory, it is believed that by utilizing wet etching the hexagonal-shaped cross sections of the wells 112 may result using the cylindrical apertures 110 in the mask material (FIG. 3A) because phosphoric acid and/or other anisotropic etchants can remove material at different rates along different crystal planes of the first semiconductor material 106 under select etching conditions. For example, it is believed that phosphoric acid and/or other anisotropic etchants can remove GaN material from c-plane, a-plane, and/or m-plane faster than other planes (e.g., those shown in FIGS. 2D-2F) due, at least in part, to the different bonding energy of gallium (Ga) and/or nitrogen (N) atoms in these planes. As a result, phosphoric acid and/or other anisotropic etchants can preferentially remove materials from these crystal planes to form the hexagonal cross sections of the wells 112.

It is also believed that etching conditions (e.g., etching temperature, etching time, concentration and/or composition of etchant) may be adjusted to achieve different configurations for the sidewalls 114. For example, the sidewalls 114 may be formed along the same crystal planes (e.g., m-plane) based on a first set of select etching conditions. In other examples, the sidewalls 114 may be formed at different crystal planes based on a second set of select etching conditions. At least some of the sidewalls 114 may be formed at an angle that is slanted compared to the base 116. In further examples, the sidewalls 114 may converge into an apex (not shown) so that the individual wells 112 have an inverted hexagonal pyramid shape based on a third set of select etching conditions.

Even though the base 116 is shown as generally planar in FIG. 3B, in certain embodiments, the base 116 may be non-planar. For example, as shown in FIG. 3C, the wells 112 may individually include a base 116 with an inverted hexagonal pyramid shape converging at an apex 118. Techniques for forming the sidewalls 114 and the non-planar base 116 can include removing material from the first semiconductor material 106 via (1) only isotropic etching, (2) anisotropic etching to expose desired crystal planes for the sidewalls 114 and subsequent isotropic etching to form the non-planar base 116, or (3) other suitable techniques.

FIG. 3D shows another stage of the process in which an active region 120 of an LED device is formed in the semiconductor device 100. In the following description, the embodiment of the semiconductor device 100 shown in FIG. 3B is used to describe subsequent processing operations for illustration purposes. One of ordinary skill in the art will understand that the described operations, structures, and/or functions may equally apply to the embodiments shown in FIG. 3C and/or other embodiments of the semiconductor device 100. In the illustrated embodiment, the active region 120 includes InGaN/GaN MQWs. In other embodiments, the active region 120 may include other suitable semiconductor materials.

As shown in FIG. 3D, the active region 120 may include a first active portion 120 a formed on the second surface 106 b of the first semiconductor material 106, a second active portion 120 b formed on the sidewalls 114, and a third active portion 120 c on the bases 116 of the wells 112. In certain embodiments, the active region 120 may generally conform to the second surface 106 b of the first semiconductor material 106. As a result, the first, second, and third portions 120 a, 120 b, and 120 c of the active region 120 may have a generally constant thickness (and/or number of MQWs).

In other embodiments, the first, second, and third portions 120 a, 120 b, and 120 c of the active region 120 may have different thicknesses by forming the active region 120 at different rates on the different underlying surfaces of the first semiconductor material 106. For example, the sidewalls 114 of the wells 112 may be selected to form at crystal planes upon which the active region 120 may readily nucleate. Thus, the second active portion 120 b of the active region 120 may have a thickness that is greater than that of the first active portion 120 a on the second surface 106 b of the first semiconductor material 106 and/or the third active portion 120 c on the bases 116 of the wells 112.

In further embodiments, parts of the second active portion 120 b may have different thicknesses than other parts of the second active portion 120 b. As a result, different parts of the second active portion 120 b may have different indium (In) incorporation rates. For example, the active region 120 of two adjacent sidewalls 114 of a particular well 112 may have different thicknesses because the adjacent sidewalls 114 have been formed on different crystal planes. In other examples, some sidewalls 114 (e.g., two opposing sidewalls) of a particular well 112 may have the same thickness while other sidewalls 114 (e.g., two adjacent sidewalls) of the well 112 may have different thicknesses, and thus different thicknesses of MQWs. It is believed that different indium (In) incorporation and/or different thicknesses of the MQWs can influence the wavelengths and/or other optical properties of the MQWs.

Without being bound by theory, it is believed that the emission characteristics of the semiconductor device 100 are related to or at least influenced by the MQW density in the active region 120. Accordingly, several characteristics of the semiconductor device 100 may be adjusted to achieve desired emission wavelengths, colors, and/or other emission characteristics of the semiconductor device 100. For example, one may increase the pattern density (e.g., by reducing the pitch to about 50 μm to about 500 nm) of the apertures 110 (FIG. 3A) and of corresponding wells 112 to increase the interfacial areas upon which MQWs of varying optical properties may be formed. In another example, one may also increase the depth and/or aspect ratio of the wells 112 (e.g., with an aspect ratio of about 40:1) to increase the interfacial areas of the sidewalls 114. In a further example, one may also adjust the configuration of the sidewalls 114 (e.g., crystal planes) of the individual wells 112 such that the active region 120 may form with a desired number and optical properties of MQWs. In yet further examples, one may adjust a combination of at least some of the foregoing characteristics and/or other suitable characteristics of the semiconductor device 100.

FIG. 3E shows another stage of the process in which a second semiconductor material 126 is formed on the active region 120. In the illustrated embodiment, the second semiconductor material 126 includes a P-type GaN material. In other embodiments, the second semiconductor material 126 may include an N-type GaN material and/or other suitable semiconductor materials.

As shown in FIG. 3E, the second semiconductor material 126 includes first, second, and third semiconductor portions 126 a, 126 b, and 126 c generally corresponding to the first, second, and third active portions 120 a, 120 b, and 120 c of the active region 120. As a result, the second semiconductor material 126 includes a plurality of openings 128 individually extending into the wells 112. In other embodiments, the second semiconductor material 126 may completely fill the wells 112 to create a generally planar surface (not shown) spaced apart from the active region 120. For any of the foregoing embodiments, techniques for forming the first semiconductor material 106, the active region 120, and the second semiconductor material 126 can include MOCVD, MBE, LPE, and/or other suitable techniques.

FIG. 3F shows another stage of the process in which an electrode material 130, a reflective material 132, and a diffusion barrier 134 are formed on the semiconductor device 100 in series. The electrode material 130 substantially fills the wells 112 and has a generally planar electrode surface 130 a proximate to the reflective material 132. The electrode material 130 can include indium tin oxide (ITO), fluorine-doped tin oxide (FTO), zinc oxide (ZnO), and/or other suitable transparent conducting oxides (“TCOs”). The reflective material 132 can include silver (Ag), aluminum (Al), and/or other suitable light reflective materials. The diffusion barrier 134 can include silicon carbide (SiC), silicon oxide (SiO₂), and/or other suitable insulating materials. Techniques for forming the electrode material 130, the reflective material 132, and the diffusion barrier 134 may include PVD, CVD, ALD, spin coating, and/or other suitable techniques.

FIG. 3G shows another stage of the process in which the microelectronic substrate 102 and the optional first and second buffering materials 104 a and 104 b are removed from the semiconductor device 100. In FIG. 3G, the semiconductor device 100 is shown inverted related to FIG. 3E for illustrating a suitable processing orientation. Techniques for removing these materials can include back grinding, wet etching, dry etching, laser ablation, and/or other suitable techniques.

FIG. 3H shows an optional stage of the process in which a plurality of light extraction features 140 are formed on the first semiconductor material 106. In the illustrated embodiment, the light extraction features 140 includes a plurality of hexagonal pyramids formed via wet etching (e.g., with phosphoric acid) the first semiconductor material 106. In other embodiments, the light extraction features 140 may include other suitable structures. In further embodiments, the light extraction features 140 may be omitted.

In operation, the active region 120 may generate emissions when an excitation voltage is applied via the first and second semiconductor materials 106 and 126. As shown in FIG. 3G, the first, second, and third portions 120 a, 120 b, and 120 c of the active region 120 can individually generate corresponding first, second, and third emission portions 150 a, 150 b, and 150 c. As a result, several embodiments of the semiconductor device 100 can generate more emissions (e.g., from the second portion 120 b of the active region 120) when compared to others planar LEDs, which can only emit from planar portions corresponding to the first and third portions 120 a and 120 c of the active region 120.

Without being bound by theory, it is believed that embodiments of the first and second semiconductor materials 106 and 126 may form optical guides for light generated by the active region 120 during operation. It is believed that the differences in refractive indices between the first and second semiconductor materials 106 and 126 and the active region 120 may reduce the amount of internal reflection in the wells 112. As a result, the first and second semiconductor materials 106 and 126 may “guide” an increased amount of light generated by the active region 120 to outwardly toward an illumination target.

Several embodiments of the semiconductor device 100 may increase the emission power per unit area over conventional LEDs. As shown in FIG. 1, conventional LEDs typically include planar N-type and/or P-type GaN materials 14 and 18. Such planar structures have limited interface area and thus can limit the number of quantum wells formed thereon to a footprint area of W×L (FIG. 3G). As a result, the emission output from the conventional LEDs may be limited. By forming three-dimensional wells 112 (FIG. 3B) in the first semiconductor material 106, the interfacial area for forming the active region 120 can be increased as described in the following formula:

ΔA=P×D×ρ

where ΔA is the increase in interfacial area; P is perimeter of wells 112 (FIG. 3B); D (FIG. 3G) is depth of the wells 112; ρ is number of wells 112 in the footprint W×L (FIG. 3G). As a result, several embodiments of the semiconductor device 100 have higher MQW density per unit footprint area of the semiconductor device 100 than conventional LEDs to enable a higher emission power output.

Even though the wells 112 are shown in FIGS. 3B-3H as having hexagonal cross sections, in other embodiments, the wells 112 may also have pentagonal, circular, oval, rectilinear, square, triangular, and/or other suitable cross sections that are formed via dry etching and/or other suitable techniques. In further embodiments, the wells 112 may individually have a combination of cross sectional shapes that are formed via, e.g., multiple dry etching operations. In yet further embodiments, at least some of the wells 112 may have different geometric and/or other characteristics different from other wells 112.

From the foregoing, it will be appreciated that specific embodiments of the technology have been described herein for purposes of illustration, but that various modifications may be made with other embodiments in addition to or in lieu of the elements of the other embodiments.

Accordingly, the disclosure is not limited except as by the appended claims. 

I/We claim:
 1. A light emitting diode, comprising: a semiconductor material having a first surface and a second surface opposite the first surface; and an active region in direct contact with at least a part of the second surface of the semiconductor material, the active region including a first portion and a second portion, the first and second portions forming a non-planar three-dimensional structure.
 2. The light emitting diode of claim 1 wherein the second surface of the semiconductor material is non-planar, and wherein the active region generally conforms to the second surface of the semiconductor material.
 3. The light emitting diode of claim 1 wherein the first and second portions of the active region are spaced apart by a third portion therebetween, the first, second, and third portions forming a non-planar three-dimensional structure.
 4. The light emitting diode of claim 1 wherein the first and second portions of the active region are spaced apart by a third portion therebetween, the first, second, and third portions forming a non-planar three-dimensional structure, and wherein at least one of the first, second, and third portions is at an angle of less than about 180° with respect to the other portions.
 5. The light emitting diode of claim 1 wherein the first and second portions of the active region are spaced apart by a third portion therebetween, the first, second, and third portions forming a non-planar three-dimensional structure, and wherein at least one of the first, second, and third portions is at an angle of about 90° with respect to at least one of the other portions.
 6. A light emitting diode, comprising: a GaN material having a first surface and a second surface opposite the first surface, the GaN material carrying an array of wells that each individually has an opening at least proximate to the first surface, the individual wells extending at least partially into the GaN material toward the second surface; and an active region in direct contact with the semiconductor material, at least a portion of the active region being in the individual array of wells carried by the GaN material.
 7. The light emitting diode of claim 6 wherein the individual wells include a sidewall between the opening and a base proximate to the second surface of the semiconductor material.
 8. The light emitting diode of claim 18 wherein: the individual wells each include a sidewall between the opening and a base proximate to the second surface of the semiconductor material; and at least one base has a configuration different from the other bases of the other wells.
 9. The light emitting diode of claim 6 wherein: the individual wells each include a sidewall between the opening and a base proximate to the second surface of the semiconductor material; and at least one base is generally planar while the other bases are non-planar.
 10. The light emitting diode of claim 6 wherein: the individual wells each include a sidewall between the opening and a base proximate to the second surface of the semiconductor material; and the bases of the wells have generally similar configurations.
 11. The light emitting diode of claim 6 wherein: the individual wells each include a sidewall between the opening and a base proximate to the second surface of the semiconductor material; and the bases of the wells are either generally planar or non-planar. 